10% 20% 30% glass fiber reinforced abs plastic raw materials
ABS resin has good mechanical properties and forming properties, and its large application fields are automotive, electronic appliances and building materials.In addition, it is widely used in packaging, furniture, sports and entertainment products, machinery and instrument industries.
Minimum order quantity
1 | |
10% 20% 30% glass fiber reinforced abs plastic raw materials
| Brand Name: | HENGA | ||
| Color: | NATURE | ||
| Model Number: | JLX-ABS-GF001 | ||
| Certificates: | REACH, ROHS, TS16949 | ||
| Usage: | Home applicances, Automotive, Electronics, New Energy Vehicles | ||
| Delivery time: | 3-5days | ||
| Physical | Nominal Value | Unit | Test Method |
| Density / Specific Gravity | |||
| -- | 1.07 to 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.10 to 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 3.0 to 16 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 0.20 to 27 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 3.98 to 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.093 to 0.37 | % | ASTM D955 |
| Across Flow : 23°C | 0.38 to 0.60 | % | ASTM D955 |
| 23°C | 0.18 to 0.40 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 23°C | 0.050 to 0.35 | % | ASTM D570 |
| 24 hr, 23°C | 0.030 to 0.32 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 to 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness | |||
| 23°C | 101 to 126 | ASTM D785 | |
| 23°C | 109 to 118 | ISO 2039-2 | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | |||
| 23°C | 58.0 to 9830 | MPa | ASTM D638 |
| 23°C | 3550 to 8890 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 35.7 to 99.4 | MPa | ASTM D638 |
| Yield, 23°C | 43.0 to 114 | MPa | ISO 527-2 |
| Break, 23°C | 37.6 to 98.5 | MPa | ASTM D638 |
| Break, 23°C | 41.5 to 89.4 | MPa | ISO 527-2 |
| 23°C | 40.0 to 104 | MPa | ASTM D638 |
| 23°C | 61.2 to 100 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 to 3.6 | % | ASTM D638 |
| Break, 23°C | 1.9 to 5.2 | % | ASTM D638 |
| Break, 23°C | 1.5 to 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2170 to 8100 | MPa | ASTM D790 |
| 23°C | 3320 to 7990 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 66.3 to 146 | MPa | ASTM D790 |
| 23°C | 60.2 to 156 | MPa | ISO 178 |
| Yield, 23°C | 64.8 to 138 | MPa | ASTM D790 |
| Break, 23°C | 63.3 to 116 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 4.9 to 9.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 8.0 to 25 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 39 to 92 | J/m | ASTM D256 |
| 23°C | 3.8 to 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 230 to 410 | J/m | ASTM D256 |
| 23°C | 13 to 23 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 4.00 to 15.0 | J | ASTM D3763 |
| 23°C | 1.00 to 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 93.3 to 114 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 99.8 to 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 89.1 to 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 88.9 to 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 to 136 | °C | ASTM D1525 |
| -- | 98.8 to 111 | °C | ISO 306 |
| CLTE | |||
| Flow | 1.3E-5 to 4.5E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.2E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse | 4.3E-5 to 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 to 75.0 | °C | UL 746 |
| RTI Imp | 60.0 to 75.0 | °C | UL 746 |
| RTI Str | 60.0 to 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity | |||
| -- | 1.0E+2 to 2.5E+15 | ohms | ASTM D257 |
| -- | 1.0E+13 to 2.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+2 to 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 to 2.5E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 16 to 19 | kV/mm | ASTM D149 |
| 23°C | 23 to 37 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 398 to 600 | V | IEC 60112 |
| Hot-wire Ignition (HWI) | 120 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
| Burning Rate | 99 to 100 | mm/min | ISO 3795 |
| Glow Wire Ignition Temperature | 550 to 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
| Drying Temperature | 79 to 86 | °C | |
| Drying Time | 2.0 to 9.0 | hr | |
| Suggested Max Moisture | 0.020 to 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 184 to 252 | °C | |
| Middle Temperature | 205 to 239 | °C | |
| Front Temperature | 204 to 270 | °C | |
| Nozzle Temperature | 209 to 241 | °C | |
| Processing (Melt) Temp | 213 to 260 | °C | |
| Mold Temperature | 59 to 80 | °C | |
| Injection Pressure | 85.5 to 87.3 | MPa | |
| Back Pressure | 0.250 to 0.619 | MPa | |
| Screw Speed | 45 to 100 | rpm |